AA 6061-T4 アルミニウム合金：溶接・ろう付け・陽極酸化に適した高性能材
概要
AA 6061-T4 は、入手性に優れ、陽極酸化処理に適した良好な表面仕上げが得られるアルミニウム合金です。溶接性・ろう付け性に優れ、海水や大気環境に対する耐食性を備えています。また、熱間鍛造にも適しており、汎用性の高い構造材として広く採用されています。
物理的特性
| 特性 | 値 | 条件 | 関連規格 |
|---|---|---|---|
| 密度 | 2.7 g/cm³ | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
機械的特性
| 特性 | 値 | 条件 | 関連規格 | 備考 |
|---|---|---|---|---|
| 曲げ疲労強度 | 95.0 MPa | T4 | AA Standards | |
| 弾性係数 | 69.0 GPa | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| ブリネル硬度 | 65.0 HB | T4 | AA Standards | |
| 平面ひずみ破壊靭性 | 22.0 - 35.0 MPa·√m | - | - | 6000 系アルミニウムの典型値 |
| ポアソン比 | 0.33 | - | - | 6000 系アルミニウムの典型値 |
| せん断弾性係数 | 26.0 - 26.5 GPa | - | - | 6000 系アルミニウムの典型値 |
| 引張強さ | 180.0 MPa | T4 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
| 引張強さ | 205.0 MPa | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | |
| 引張強さ | 240.0 MPa | T4 | AA Standards |
熱的特性
| 特性 | 温度 | 値 | 条件 | 関連規格 | 備考 |
|---|---|---|---|---|---|
| 熱膨張係数 | 20 °C | 2.36×10⁻⁵ 1/K | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| 熱膨張係数 | 100 °C | 2.36×10⁻⁵ 1/K | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| 融点 | - | 580.0 - 650.0 °C | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| 比熱容量 | - | 887.0 - 963.0 J/(kg·K) | - | - | 6000 系アルミニウムの典型値 |
| 熱伝導率 | - | 155.0 - 180.0 W/(m·K) | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
電気的特性
| 特性 | 値 | 条件 | 関連規格 |
|---|---|---|---|
| 電気伝導度 | 23,000,000 - 27,000,000 S/m | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 電気抵抗率 | 3.7×10⁻⁸ - 4.35×10⁻⁸ Ω·m | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
化学組成
| 元素 | 含有量 | 条件 | 関連規格 |
|---|---|---|---|
| クロム (Cr) | 0.04 - 0.35 % | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 銅 (Cu) | 0.15 - 0.40 % | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 鉄 (Fe) | 0.70 % | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| マグネシウム (Mg) | 0.80 - 1.20 % | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| マンガン (Mn) | 0.15 % | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| シリコン (Si) | 0.40 - 0.80 % | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| チタン (Ti) | 0.15 % | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 亜鉛 (Zn) | 0.25 % | T4 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
加工・技術的特性
| 特性 | 評価 |
|---|---|
| ろう付け | 市販のプロセス・方法で可能 |
| 耐食性 | 応力腐食割れ：O, T6, T651, T652, T6510, T6511 で実用・試験ともに損傷なし。T4, T451, T4510, T4511 で実用上損傷なし、試験で限定的損傷。全般：工業雰囲気や海水雰囲気で無保護でも良好 |
| 一般的な切削加工性 | O 材：悪い、T4/T451/T4510/T4511/T6/T651/T652/T6510/T6511：十分 |
| 成形加工性 | O 材：良好、T4/T451/T4510/T4511：可、T6/T651/T652/T6510/T6511：悪い |
金属
- AA 6061 H13 アルミニウム合金：高強度、耐食性、溶接性に優れる
- AA グレード 5456 O アルミニウム標準 – 主要機械的特性
- AA規格 5083-O アルミニウム合金 - 高強度・高耐食性の標準規格
- AA 6066 T6 アルミニウム合金 - AA規格・ASTM規格準拠仕様
- AA 6351 T6 アルミニウム合金 – 技術規格と特性
- AA 6061 T89 合金 — 高グレード、耐食性に優れ加工容易
- AA 6061 T94 アルミニウム合金 – 高性能グレード6061 T94仕上げ
- AA規格グレード 5454 O – 包括的アルミニウム合金仕様
- AA規格 1060 O アルミニウム合金：完全な材料仕様と規格
- AA 3004 O材：軟質テンパーの包括的特性・性能データ
- AA 5050-O アルミニウム合金 – 規格準拠の機械的特性と用途ガイド