AA 5052-H32 アルミニウム合金：優れた耐食性と溶接性能
AA 5052は非熱処理型アルミニウム合金で、優れた仕上げ特性を備えています。ほとんどのアルミニウム合金よりも耐食性に優れ、特に海水や海洋大気環境に対する耐性が高いのが特徴です。一般的な溶接技術で容易に溶接可能であり、すべてのアルミニウム合金の中でも最高レベルの溶接特性を発揮します。
一般特性
| 特性 | 値 | 状態 | 関連規格 |
|---|---|---|---|
| 密度 | 2.68 g/cm³ | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
機械的特性
| 特性 | 値 | 状態 | 関連規格 | 備考 |
|---|---|---|---|---|
| 曲げ疲労強度 | 115.0 MPa | H32 | AA Standards | |
| 弾性係数 | 70.0 GPa | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| ブリネル硬度 | 60.0 | H32 | AA Standards | |
| 平面ひずみ破壊靭性 | 22.0 - 35.0 MPa·√m | - | - | 圧延5000系アルミニウムの典型値 |
| ポアソン比 | 0.33 | - | - | 圧延5000系アルミニウムの典型値 |
| せん断弾性係数 | 26.0 - 26.5 GPa | - | - | 圧延5000系アルミニウムの典型値 |
| 引張強さ | 215.0 - 265.0 MPa | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
| 引張強さ | 215.0 MPa | H32 | AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | |
| 引張強さ | 215.0 - 255.0 MPa | H32 | AA Standards, ASTM B316 | |
| 引張強さ | 230.0 MPa | H32 | AA Standards |
熱的特性
| 特性 | 温度 | 値 | 状態 | 関連規格 | 備考 |
|---|---|---|---|---|---|
| 熱膨張係数 | 20 °C | 2.38×10⁻⁵ 1/K | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 熱膨張係数 | 100 °C | 2.38×10⁻⁵ 1/K | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 最高使用温度 | - | 150.0 °C | - | - | 圧延5000系アルミニウムの典型値 |
| 融点 | - | 605.0 - 650.0 °C | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 比熱容量 | - | 879.0 - 963.0 J/(kg·K) | - | - | 圧延5000系アルミニウムの典型値 |
| 熱伝導率 | - | 138 W/(m·K) | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
電気的特性
| 特性 | 値 | 状態 | 関連規格 |
|---|---|---|---|
| 電気伝導度 | 20,000,000 S/m | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 電気抵抗率 | 5×10⁻⁸ Ω·m | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
化学組成
| 元素 | 含有量 | 状態 | 関連規格 |
|---|---|---|---|
| クロム | 0.15 - 0.35 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 銅 | 0.1 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 鉄 | 0.40 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| マグネシウム | 2.2 - 2.8 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| マンガン | 0.1 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| シリコン | 0.25 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 亜鉛 | 0.1 % | H32 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
技術的特性
| 特性 | 評価 |
|---|---|
| ろう付け | 一般的：制限付きろう付け |
| 耐食性 | 応力腐食割れ：運転中および実験室試験で損傷なし、一般的：非常に良好、産業雰囲気や海水雰囲気で無保護でも使用可能 |
| 一般的切削性 | 一般的：不良（O, H32）、十分（H34, H36, H38） |
| 加工性 | 一般的（状態）：良好（O）、許容（H32, H34）、不良（H36, H38） |
金属
- AA規格 5056 H32 - 包括的な技術概要
- ASTM B316 グレード 5052 H32 アルミニウム — 優れた耐食性と溶接性能
- ASTM B483 グレード 5052 H32 – プレミアム マリングレード アルミニウム合金
- ASTM B211 5052 H32アルミニウム合金：優れた耐食性と溶接性
- ASTM B210 5052 H32アルミニウム - 優れた耐食性と溶接性を持つ船舶・海洋用合金
- ASTM B234M 5052-H32 アルミニウム合金：優れた耐食性・溶接性を持つ非熱処理型材
- AA グレード 5456 O アルミニウム標準 – 主要機械的特性
- AA規格 5083-O アルミニウム合金 - 高強度・高耐食性の標準規格
- AA 6066 T6 アルミニウム合金 - AA規格・ASTM規格準拠仕様
- AA 6351 T6 アルミニウム合金 – 技術規格と特性
- AA 規格 5456 H32 アルミニウム：主要な機械的・物理的特性